Basic Info.
Model NO.
Backing compound
Material
Epoxy
Classification
Room Curing
Main Agent Composition
Epoxy
Characteristic
Waterproof
Promoter Composition
Epoxy
Composition
Organic Material
Color
Grey
Name
Ceramic Epoxy
Certificate
MSDS, TDS
OEM Service
Yes
Shelf Life
1 Year
Capacity
30000tons/Month
Curing Time
7 Hr
Maximum Operating Temperature
+250 °f
Package Quantity
1 Per Case
Product Form
Putty
Resistant Properties
Corrosion-Resistant
Transport Package
Carton Case
Specification
10kg/set, 20kg/set
Trademark
Higlue
Origin
China
Production Capacity
1000 PCS a Week
Product Description
Rugged Alloy Steel Casting Mining Machinery Parts Cone Crusher Liner Filler Mantle Backing Compound
The filling material is a two-component epoxy based filler with high density, high impact resistance and low shrinkage, which is developed based on the Polycon composite technology platform. It is used for filling and sealing the gap between the lining plate and the body of cone type or rotary crusher, providing high impact resistance on the back, protecting the lining plate from impact damage and extending the service life, which is the preferred measure for many mine crushing workshops.
Instructions for use:
Company profile:
Jiangxi Gooz Adhesive Co.,Ltd,is a leading manufacturer of industrial adhesive products
established in 1996,the adhesive products main is sell to foreign country,and received
many praises.Our main products:
Threadlocker,pipe thread sealing cord,intant adhesive,epoxy adhesive,tile adhesive
surface treatmet etc..
FAQ
Description:
Use: Rotary crusher, cone crusher, ball mill and other lining plate or equipment base need gap sealing, casting filling, reinforcement occasions.
Product features: Excellent impact resistance on the back Low shrinkage rate High strength and toughness Adapted to wide weather conditions Low temperature curing speed is fast Good liquidity
Typical application: Rough breaking, medium breaking and fine breaking in mine crushing workshop
Specification
The following technical parameters are for reference only and do not serve as technical specifications. Temperature 20ºC
| color | Milky white | Test standard |
| Mixing ratio (weight) | Principal agent 10: curing agent 1 | |
| Operating time (23ºC) | 15-20 minutes | |
| Curing time (23ºC) | 4-6 hours | |
| Compressive strength | >165MPa | ASTM D695 |
| Impact strength | > 13.5 KJ/m2 | ISO179 |
| Shear strength | >361kg | ASTM D790 |
| Tensile strength | 47.3 MPa | ASTM D638 |
| density | 1500kg/ m3 | |
| Hardness after curing (Shaw D) | 89 | ASTM D2240 |
| viscosity | 16000cps | |
| Shrinkage rate | 0.01% |
Instructions for use:
Polycon backlining filler is an epoxy resin based backlining material, consisting of components A and B. In low temperature and cold areas, it needs to be stored at room temperature for 24 hours before use. At low temperature, the viscosity will become larger, and when the temperature exceeds 30 degrees Celsius, the operation time will become shorter and the reaction curing speed will be accelerated. When the temperature is below 10 degrees, the corresponding curing time is extended Mixed specification Mixing ratio weight ratio (main agent: hardener) 10:1, this product hardener for two parts, easy to mix according to the actual dosage, so as not to cause waste. It is strongly recommended to mix all at once with one part of the hardener on. 1. When stirring, the main agent and curing agent can be mixed according to the weight ratio of 10:1, and the curing agent can be added to the main agent. 2. Use a blender to stir the material thoroughly (continuously scraping the side and bottom mixture of the container) until it is evenly mixed, but the time should not exceed 10 minutes.
Jiangxi Gooz Adhesive Co.,Ltd,is a leading manufacturer of industrial adhesive products
established in 1996,the adhesive products main is sell to foreign country,and received
many praises.Our main products:
Threadlocker,pipe thread sealing cord,intant adhesive,epoxy adhesive,tile adhesive
surface treatmet etc..